SWCNT Applications Conductive Rubber
Conductive Silicone Rubber (TS 800C Series)
Colorable conductive and anti-static silicone rubber made with SWCNT masterbatch, achieving surface resistance of 10E3–10 Ω/sq.
Key Benefits
- Low hardness possible (Shore A 10–90)
- Wide range of colors
- Surface resistance 10E3–10 Ω/sq
- Wide service temperature
- Suitable for molding and extrusion
- No black marks or migration
Applications
- OA roller
- Sheet
- Pad
- Gasket
- Hose
- Cable
Cure Systems
Molding · Radical cure (organic peroxides)
- High molding temperature
- Low compression set
- High elongation and tensile strength
Extrusion · Addition cure (Pt catalyst)
- Almost no decomposition by-products
- Excellent tear strength
- Suitable for medical and food-contact rubber parts
Molding · Low Conductive (TS 811 CL)Surface resistance 10E8–10 Ω/sq
| Product | TS 811/20CL | TS 811/30CL | TS 811/40CL | TS 811/50CL | TS 811/60CL | TS 811/70CL | TS 811/80CL | |
|---|---|---|---|---|---|---|---|---|
| Properties | Unit | Value | ||||||
| Appearance, ASTM E1767 | - | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) |
| Williams Plasticity, ASTM D926 | mm/100 | 100 | 140 | 180 | 210 | 240 | 280 | 300 |
| Specific gravity, ASTM D792 | - | 1.08 | 1.10 | 1.13 | 1.15 | 1.18 | 1.20 | 1.23 |
| Hardness, ASTM D2240 | Shore A | 20 | 30 | 40 | 50 | 60 | 70 | 80 |
| Tensile Strength, ASTM D412 | kgf/cm² | 65 | 80 | 82 | 87 | 87 | 84 | 82 |
| Elongation at Break, ASTM D412 | % | 850 | 700 | 600 | 450 | 350 | 280 | 220 |
| Tear strength, Type C ,ASTM D624 | KN/m | 13 | 18 | 21 | 25 | 24 | 22 | 21 |
| Surface Resistance , ASTM D257 | Ohm/Sq | 10E 8~9 | 10E 8~9 | 10E 8~9 | 10E 8~9 | 10E 8~9 | 10E 8~9 | 10E 8~9 |
← Swipe the table sideways →
Properties obtained using 1.2 part of SC-8B(50P)(2,5-bis(tert-butylperoxy)-2,5-dimethyl hexane) on 2mm thick slabs: molded 10 minutes at 170℃ and post-cured 4hours at 200℃. * TS 100 Series [general molding] + ACM SS-3 [SWCNT masterbatch]
Molding · Semi-Conductive (TS 811 CS)Surface resistance 10E4–6 Ω/sq
| Product | TS 811/20CS | TS 811/30CS | TS 811/40CS | TS 811/50CS | TS 811/60CS | TS 811/70CS | TS 811/80CS | |
|---|---|---|---|---|---|---|---|---|
| Properties | Unit | Value | ||||||
| Appearance, ASTM E1767 | - | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) |
| Williams Plasticity, ASTM D926 | mm/100 | 110 | 145 | 180 | 210 | 240 | 280 | 300 |
| Specific gravity, ASTM D792 | - | 1.08 | 1.10 | 1.13 | 1.15 | 1.18 | 1.20 | 1.23 |
| Hardness, ASTM D2240 | Shore A | 20 | 30 | 40 | 50 | 60 | 70 | 80 |
| Tensile Strength, ASTM D412 | kgf/cm² | 65 | 80 | 83 | 88 | 90 | 86 | 82 |
| Elongation at Break, ASTM D412 | % | 820 | 710 | 610 | 420 | 350 | 270 | 210 |
| Tear strength, Type C ,ASTM D624 | KN/m | 13 | 18 | 22 | 26 | 24 | 22 | 20 |
| Surface Resistance , ASTM D257 | Ohm/Sq | 10E 4~6 | 10E 4~6 | 10E 4~6 | 10E 4~6 | 10E 4~6 | 10E 4~6 | 10E 4~6 |
← Swipe the table sideways →
Properties obtained using 1.2 part of SC-8B(50P)(2,5-bis(tert-butylperoxy)-2,5-dimethyl hexane) on 2mm thick slabs: molded 10 minutes at 170℃ and post-cured 4hours at 200℃. * TS 100 Series [general molding] + ACM SS-3 [SWCNT masterbatch]
Molding · High Conductive (TS 811 CH)Surface resistance 10E1–3 Ω/sq
| Product | TS 811/20CH | TS 811/30CH | TS 811/40CH | TS 811/50CH | TS 811/60CH | TS 811/70CH | TS 811/80CH | |
|---|---|---|---|---|---|---|---|---|
| Properties | Unit | Value | ||||||
| Appearance, ASTM E1767 | - | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) |
| Williams Plasticity, ASTM D926 | mm/100 | 115 | 150 | 185 | 220 | 250 | 290 | 320 |
| Specific gravity, ASTM D792 | - | 1.09 | 1.11 | 1.14 | 1.16 | 1.18 | 1.21 | 1.23 |
| Hardness, ASTM D2240 | Shore A | 21 | 31 | 41 | 51 | 61 | 71 | 81 |
| Tensile Strength, ASTM D412 | kgf/cm² | 65 | 79 | 82 | 86 | 87 | 84 | 81 |
| Elongation at Break, ASTM D412 | % | 830 | 720 | 640 | 440 | 380 | 270 | 210 |
| Tear strength, Type C ,ASTM D624 | KN/m | 13 | 17 | 23 | 26 | 23 | 21 | 19 |
| Surface Resistance , ASTM D257 | Ohm/Sq | 10E 3 | 10E 3 | 10E 3 | 10E 3 | 10E 3 | 10E 3 | 10E 3 |
← Swipe the table sideways →
Properties obtained using 1.2 part of SC-8B(50P)(2,5-bis(tert-butylperoxy)-2,5-dimethyl hexane) on 2mm thick slabs: molded 10 minutes at 170℃ and post-cured 4hours at 200℃. * TS 100 Series [general molding] + ACM SS-3 [SWCNT masterbatch]
Extrusion · Low Conductive (TS 833 CL)Surface resistance 10E8–10 Ω/sq
| Product | TS 833/20CL | TS 833/30CL | TS 833/40CL | TS 833/50CL | TS 833/60CL | TS 833/70CL | TS 833/80CL | |
|---|---|---|---|---|---|---|---|---|
| Properties | Unit | Value | ||||||
| Appearance, ASTM E1767 | - | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) |
| Williams Plasticity, ASTM D926 | mm/100 | 100 | 160 | 210 | 240 | 250 | 270 | 310 |
| Specific gravity, ASTM D792 | - | 1.08 | 1.08 | 1.10 | 1.13 | 1.15 | 1.18 | 1.21 |
| Hardness, ASTM D2240 | Shore A | 21 | 33 | 41 | 51 | 61 | 68 | 77 |
| Tensile Strength, ASTM D412 | kgf/cm² | 76 | 87 | 94 | 107 | 112 | 112 | 107 |
| Elongation at Break, ASTM D412 | % | 810 | 720 | 680 | 600 | 540 | 450 | 400 |
| Tear strength, Type C ,ASTM D624 | KN/m | 18 | 26 | 28 | 30 | 32 | 31 | 27 |
| Surface Resistance , ASTM D257 | Ohm/Sq | 10E 8~9 | 10E 8~9 | 10E 8~9 | 10E 8~9 | 10E 8~9 | 10E 8~9 | 10E 8~9 |
← Swipe the table sideways →
Properties obtained using addition cure system (Platinum catalyst) on 2mm thick slabs: molded 5 minutes at 120℃ and post-cured 4hours at 200℃. * TS 333 Series [general extrusion] + ACM SS-3 [SWCNT masterbatch]
Extrusion · Semi-Conductive (TS 833 CS)Surface resistance 10E4–6 Ω/sq
| Product | TS 833/20CS | TS 833/30CS | TS 833/40CS | TS 833/50CS | TS 833/60CS | TS 833/70CS | TS 833/80CS | |
|---|---|---|---|---|---|---|---|---|
| Properties | Unit | Value | ||||||
| Appearance, ASTM E1767 | - | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) |
| Williams Plasticity, ASTM D926 | mm/100 | 110 | 160 | 210 | 240 | 250 | 270 | 310 |
| Specific gravity, ASTM D792 | - | 1.08 | 1.08 | 1.11 | 1.14 | 1.16 | 1.19 | 1.22 |
| Hardness, ASTM D2240 | Shore A | 21 | 33 | 41 | 50 | 60 | 67 | 77 |
| Tensile Strength, ASTM D412 | kgf/cm² | 79 | 85 | 96 | 109 | 111 | 108 | 104 |
| Elongation at Break, ASTM D412 | % | 800 | 730 | 680 | 590 | 520 | 420 | 370 |
| Tear strength, Type C ,ASTM D624 | KN/m | 19 | 25 | 29 | 32 | 31 | 30 | 27 |
| Surface Resistance , ASTM D257 | Ohm/Sq | 10E 4~6 | 10E 4~6 | 10E 4~6 | 10E 4~6 | 10E 4~6 | 10E 4~6 | 10E 4~6 |
← Swipe the table sideways →
Properties obtained using addition cure system (Platinum catalyst) on 2mm thick slabs: molded 5 minutes at 120℃ and post-cured 4hours at 200℃. * TS 333 Series [general extrusion] + ACM SS-3 [SWCNT masterbatch]
Extrusion · High Conductive (TS 833 CH)Surface resistance 10E1–3 Ω/sq
| Product | TS 833/20CH | TS 833/30CH | TS 833/40CH | TS 833/50CH | TS 833/60CH | TS 833/70CH | TS 833/80CH | |
|---|---|---|---|---|---|---|---|---|
| Properties | Unit | Value | ||||||
| Appearance, ASTM E1767 | - | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) | Black (colorable) |
| Williams Plasticity, ASTM D926 | mm/100 | 110 | 150 | 210 | 240 | 250 | 270 | 310 |
| Specific gravity, ASTM D792 | - | 1.08 | 1.08 | 1.12 | 1.15 | 1.16 | 1.20 | 1.22 |
| Hardness, ASTM D2240 | Shore A | 22 | 32 | 40 | 50 | 60 | 68 | 77 |
| Tensile Strength, ASTM D412 | kgf/cm² | 77 | 83 | 92 | 106 | 107 | 105 | 102 |
| Elongation at Break, ASTM D412 | % | 840 | 720 | 660 | 560 | 510 | 400 | 340 |
| Tear strength, Type C ,ASTM D624 | KN/m | 18 | 23 | 27 | 31 | 30 | 30 | 25 |
| Surface Resistance , ASTM D257 | Ohm/Sq | 10E 3 | 10E 3 | 10E 3 | 10E 3 | 10E 3 | 10E 3 | 10E 3 |
← Swipe the table sideways →
Properties obtained using addition cure system (Platinum catalyst) on 2mm thick slabs: molded 5 minutes at 120℃ and post-cured 4hours at 200℃. * TS 333 Series [general extrusion] + ACM SS-3 [SWCNT masterbatch]