SWCNT Applications Conductive Rubber
MWCNT Conductive Silicone Rubber
Conductive silicone rubber (TS 811 MW · TS 833 MW Series) using multi-wall carbon nanotubes to reach a volume resistivity of 10E0–2 Ω·cm.
Key Benefits
- Volume resistivity 10E0–2 Ω·cm
- Wide service temperature
- Suitable for molding and extrusion
- Reduced black marks and migration
Applications
- OA roller
- Sheet
- Pad
- Gasket
- Hose
- Cable
Cure Systems
Molding · Radical cure (organic peroxides)
- High molding temperature
- Low compression set
- High elongation and tensile strength
Extrusion · Addition cure (Pt catalyst)
- Almost no decomposition by-products
- Excellent tear strength
- Suitable for medical and food-contact rubber parts
Extrusion · High ConductiveVolume resistivity 1–3 Ω·cm
| Product | MWCNT | CARBON BLACK + MWCNT | |||
|---|---|---|---|---|---|
| Product | TS 833/50 MW | TS 833/70 MW | TS 833/50 MW(C) | TS 833/70 MW(C) | |
| Properties | Unit | Value | |||
| Appearance, ASTM E1767 | - | Black | Black | Black | Black |
| Williams Plasticity, ASTM D926 | mm/100 | 450 | 500 | 450 | 550 |
| Specific gravity, ASTM D792 | - | 1.12 | 1.14 | 1.10 | 1.18 |
| Hardness, ASTM D2240 | Shore A | 50 | 70 | 50 | 70 |
| Tensile Strength, ASTM D412 | kgf/cm² | 92 | 102 | 71 | 71 |
| Elongation at Break, ASTM D412 | % | 700 | 500 | 400 | 350 |
| Tear strength, Type C ,ASTM D624 | KN/m | 45 | 49 | 25 | 27 |
| Volume Resistance ,ASTM D257 | Ohm∙cm | 3 | 2.5 | 3 | 1.5 |
← Swipe the table sideways →
Properties obtained using addition cure system (Platinum catalyst) on 2mm thick slabs: molded 5 minutes at 120℃ and post-cured 4 hours at 200℃.
Product Photo
MWCNT Conductive Silicone Rubber